galvanized iron section properties tables

huangyhg

galvanized iron section properties tables
does anyone know of a resource on galvanized iron shapes tables? any leads will be appreciated.

are you talking about normal structural shapes which are galvanized?
yes, i would like to know if there are any factors that increase or decrease allowable stresses.
rarebug,
by your posts i assume you are talking about structural steel, not iron.
for normal structural grade steel (36 ksi to 50 ksi) the galvanising process does not have any significant effects on the properties. design them as per normal steel sections.
check out
yes, i was thinking about steel (iron plus carbon galvanized)
thank you csd72!!